Impact Modified Low-Temperature PP Pellets DGK-PP 66D
Toughened PP for low-temperature use with 450% elongation at break
Impact modified PP for low-temperature use; elongation at break 450%, flexural modulus 1100 MPa, notched impact strength 49 kJ/m2 at 23°C and 13 kJ/m2 at -23°C.
Low-temperature impact modified PP compound DGK-PP 66D with 450% elongation at break for cold-use structural parts, outdoor components, automotive parts, sports equipment, appliance housings and molded products needing toughness. DEYU supports custom formulas, sample validation, bulk purchase and wholesale procurement.
Important parameters
- Base resin
- PP
- Model
- DGK-PP 66D
- Color
- Custom color matching supported
- Processing
- Injection molding. Injection molding, extrusion or other processes according to the formula.
- Key performance
- Impact modified PP for low-temperature use; elongation at break 450%, flexural modulus 1100 MPa, notched impact strength 49 kJ/m2 at 23°C and 13 kJ/m2 at -23°C.
- Status
- Pellet compound
FAQ
Can this material be color matched?
Yes. DEYU can match black, natural, white or custom colors according to the base resin, filler system and target appearance.
Can the key performance be customized?
Yes. DEYU can adjust strength, flow, color, filler system and special properties according to the part drawing and test conditions.
Can international orders receive certification documents?
Yes. DEYU can provide material data sheets and common export documents, and can coordinate RoHS, REACH, UL-related or other third-party testing according to the order requirement.
How can I get a sample of DGK-PP 66D or a similar material?
Submit the target resin, color, process and performance range. DEYU will suggest a sample grade or prepare a trial formula for sample validation. Request sample
Application areas
| Application area | Typical parts |
|---|---|
| Application area 1 | cold-chain box fittings |
| Application area 2 | outdoor clips |
| Application area 3 | sports equipment housings |
| Application area 4 | automotive interior clips |
| Application area 5 | low-temperature tool handles |
| Application area 6 | winter-use buckles |
Reference quote
- Minimum price
- USD 5.9/kg
- Maximum price
- USD 10.8/kg
- Delivery
- Tax-included reference price; freight is not included.
- Stock
- Standard stock reference: 1000 kg. Special color, performance or certification requirements require custom production.
Final quotation depends on the specific formula, color, order volume and testing requirements.
Data sheet
Physical Property Data Sheet
| Name | DGK-PP 66D | Specification | DGK-PP 66D |
|---|---|---|---|
| Material properties | Impact modified, low-temperature resistant | Color | Natural |
| Use | Sports equipment, automotive parts | Sample state | Pellets |
| Processing method | Injection molding | - | / |
| Item | Condition | Method | Data | Unit |
|---|---|---|---|---|
| Mechanical Properties | ||||
| Tensile strength | / | ISO 527-2 | 27.5 | MPa |
| Elongation at break | / | ISO 527-2 | 450 | % |
| Flexural modulus | / | ISO 178 | 1100 | MPa |
| Notched impact strength of cantilever beam | 23℃ | ISO 180/1A | 49 | kJ/m2 |
| Notched impact strength of cantilever beam | -23℃ | GB/T 1843 | 13 | kJ/m2 |
| Others | ||||
| Density | / | ISO 1183 | 0.90 | g/cm3 |
| Melt Flow Index | / | ISO 1133 | 2 | g/10 min |
| Rockwell hardness | / | ISO 2039-2 | 95 | R |
| Heat distortion temperature | 1.8 MPa, annealed | ISO 75-2 | 110 | ℃ |
| Vicat softening point | / | ISO 306/A50 | 145 | ℃ |
| Flammability | UL-94 | / | HB | / |
| Injection molding process | ||||
| Drying temperature | 80℃ | Drying time | 4-5 h | |
| Injection temperature | 190-215℃ | Mold temperature | 80℃ | |
Contact
Focused on modified plastic R&D and production
We provide professional customization services. If you have material questions, selection difficulties or performance requirements, contact us through any method on the right.
- Email: market@deyuplastics.com
- WeChat: mkx13905842100
- WhatsApp: +86 13905842100+86 15325909695
- Telegram: @deyuplast1